Component | Wt.% | Component | Wt.% | Component | Wt.% |
C | ≤ 0.03 | Si | ≤ 1.0 | Mn | ≤ 2.0 |
P | ≤ 0.045 | S | ≤ 0.03 | Cr | 17.0-19.0 |
Mo | 2.5-3.0 | Ni | 12.5-15.0 |
State | annealed |
Density | 8.0 g/cm3 |
Hardness, Vickers | 230 HV |
Tensile strength, ultimate | 500-700 MPa |
Tensile strength, yield | 290 |
0.2% Yield stress | ≥ 200 MPa |
Elongation, break | 40% |
Modulus of elasticity | 200 GPa |
Coef. of lin. therm expansion | 16.0 E-6/°C | 20°C-100°C |
Coef. of lin. therm expansion | 17.0 E-6/°C | 20°C-300°C |
Specific heat capacity | 0.50 J/(g .K) |
|
Thermal conductivity | 15 W/(m.K) | |
Continuous use temperature | 350°C | |
Max service temperature, air | 925°C |
Resistivity | 0.75 E-4 Ohm.cm |